Company Details


  •  [Zhejiang,China]
  • Business Type:Manufacturer
  • Main Mark: Americas , Asia , East Europe , Europe , North Europe , Other Markets , West Europe
  • Exporter:91% - 100%
  • Certs:ISO/TS16949
  • Description:Auto Aluminum Transimission Part,Auto Die Casting Mounting,Auto Transimission Mounting
Inquiry Basket ( 0 )


Auto Aluminum Transimission Part,Auto Die Casting Mounting,Auto Transimission Mounting

Home > Products > Auto Parts > Transmission Parts > Auto Transimission die casting Mounting

Auto Transimission die casting Mounting

Share to:  
    Payment Type: T/T
    Incoterm: FOB,CFR,CIF,FCA
    Min. Order: 4000 Piece/Pieces
    Delivery Time: 35 Days

Basic Info

Model No.: BL001

Type: Muffler Assembly

Material: Aluminum

Muffler Type: Rear Muffler

Deck: Double

Weight: 200g-3000g

Surface Finish: Polishing

Cavity Number: 1

Machine: Cold Chamber

Additional Info

Packaging: carton, PE pallet, PE flow box, steel box, wooden pallet, container

Productivity: 5300/MONTH

Brand: NONE

Transportation: Ocean,Land,Air

Place of Origin: NINGBO

Supply Ability: 60000/MONTH

Certificate: ISO/TS16949:2009

HS Code: 7616991090


Product Description

Auto transimmison Die Casting mounting .

this part is a Auto mounting applied on the transimmison, the die casting part is irregula and duplicated, so, During the actual production, the following problems may be produced after processing

A,Surface bubble.

when Aluminum alloy in the pressure chamber fullness is too low, the volume of air pressure is too fast.The mold exhaust is bad, the aluminum alloy liquid does not exhaust. If the melting temperature is too high, the exhaust tank should be increased, the mold temperature at the bubble point will be reduced, and the degassing and slag removal of the aluminum alloy liquid will be strengthened.

If the mold temperature is too low, the aluminum liquid cooling time is too fast, open top products, the need to increase the dwell time, don't be too quick to open, full combustion. Reduce the concentration of mold release agent.

B,Shape deformation

if product structure is unreasonable, will cause uneven contraction, if mold is opened too fast, the product does not have complete solidification cooling, it is necessary to change the product structure, adjust the mold opening time. otherwise, will cause shape deformation

Material: A380
Cavity Number: 1
Process Technology: High pressure die casting, Cold Chamber
Product Dimensions: Customized
Casting General Tolerance: Grade GB-CT4
Surface Finish: Polishing
Flow Processes: Die casting, Degating to remove the residual of the gate, Polishing and Deburring to remove the burrs, Polishing to remove the parting line, flash, High Precision CNC Lathe Machining, Cleaning, Packaging, Storaging, Shipping
Control Measure: Incoming Material Test, First Article inspection, Routing inspection, Final item inspection, and Outgoing quality control
Inspection Equipment: CMM, Caliper, Plug Gage, Screw Gauge
Application: Machinery Parts
Certificate: ISO/TS16949:2009
Lead Time: 30-35 days
Trade Term: FOB Ningbo


CNC work shop

CMM facility

Looking for ideal Auto Aluminum Transimission Part Manufacturer & supplier ? We have a wide selection at great prices to help you get creative. All the Auto Die Casting Mounting are quality guaranteed. We are China Origin Factory of Auto Transimission Mounting. If you have any question, please feel free to contact us.

Product Categories : Auto Parts > Transmission Parts

Product Images
  • Auto Transimission die casting Mounting
Email to this supplier
  • *Subject:
  • *Messages:
    Your message must be between 20-8000 characters
Communicate with Supplier?Supplier
sunny Ms. sunny
What can I do for you?
Chat Now Contact Supplier